Calcium EP 2 Grease is an extreme pressure, mineral oil base, high dropping point lithium grease exhibiting a good water resistance. Its stringy adhesive character provides an extended lubricating film and thereby, suits particularly severe applications.
Calcium EP 2 Grease is used in a ball and plain bearings, joints and general applications and is Recommended for heavy industry, civil engineering, and agricultural applications.
Makes lubrication easier and more reliable.
Longer life of equipment, maintenance savings.
Very resistant lubricating film.
A good economical compromise between cost and performance.
Enhanced adherence and sealing ability.
Good resistance to centrifugation.
Water-insoluble (even in boiling water).
Extreme pressure and antiwear properties.
Good shear stability.
Typical Characteristics :
RedAppearance and textureVisual
Smooth, adhesive, tackyConsistencyNLGI
2Dropping pointASTM D566°C>185Worked X 60 strokes penetrationASTM D217mm 1/10265-295Wheel bearing test 6hrs at 135°CASTM D1263g3Oxidation bomb test, pressure dropafter 100 hrsASTM D942kPa≤504 balls EP weld loadASTM D2596kgf≥3154 balls wear test 1hr 40kg, scardiameterASTM D2266mm0,45Copper strip corrosion 24hrs at 100°CASTM D4048Rating≤1bAnti-rust Emcor testNFT 60-135Rating0 (good)
|Minimum Order Quantity||200 bucket|
|Pack Sizes LT/KG||.5,1,5,10,20,180|
Multipurpose EP3 Grease is an extreme pressure, water resistant grease manufactured using selected highly refined mineral oils, hydroxy stearate lithium soap, and special additives.
Insolubility in water
Excellent shear stability
These multipurpose greases, highly protective, EP compounded for heavy loads makes lubrication easier and more reliable:
Longer life of equipment, maintenance savings, and increase in productivity.
Very resistant lubricating film due to the high base oil viscosity. (about 140 mm²/s at 40°C)
Formulated for use in ball and roller bearings (even heavy loaded) such as in hubs (cars, transportation, agriculture, industry). Suitable for bearings, chassis, and articulations.
Multipurpose EP3 Grease, which thickener content slightly decreases pump ability must be used in big roller bearings, under moderate speeds, or severe vibration and shock conditions and also to enhance sealing properties.
Handling And Safety:
There is no risk under normal conditions of handling. The information related to prevention,
security, and health are detailed in a Material Safety Data Sheet available upon request.
TestMethodUnitAverage ResultSoap nature--LithiumColorVisual-Dark brownDropping pointASTM D566°C> 190NLGI gradeNLGINLGI3Worked X 60 strokes penetrationASTM D217mm 1/10220-250Worked X 10 000 st. penetration lossASTM D217mm 1/1015Worked X 100 000 st. penetration lossASTM D217mm 1/1035Wheel Bearing Test 130°CASTM D1263g2Four balls wear 1 h / 40 kgASTM D2266mm0,5Water Wash Out resistance at 80°CASTM D1264.mcor Rust preventionNFT 60-135Rating0-0Four balls EP Weld pointASTM D2596kgf315
|Packaging Type||Bucket, Drum, Bag, Can|
|perating temperature||15 Degree C to + 120 Degree C|
|Color and texture||Visual||-||Black, homogeneous|
|Dropping point||ASTM D566||°C||175|
|Unworked penetration||ASTM D217||1/10 mm||310|
|Worked X 60 strokes penetration||ASTM D217||1/10 mm||305|
|N.L.G.I. grade||-||-||1,5 (Between 2 grade and 1 grade)|
|Minimum Order Quantity||400 Piece|
|NLGI grade||NLGI scale||-||2|
|Dropping point (Mettler)||NFT 60-627||°C||190 (>180)|
|Unworked penetration||ISO 2137||mm 1/10||285|
|Worked X60 strokes||ISO 2137||mm 1/10||265-295|
|Worked X10 000 strokes penetration loss||ISO 2137||mm 1/10||10|
|Worked X100 000 strokes penetration loss||ISO 2137||mm 1/10||35 (<50)|
|4 balls EP weld load||ASTM D2596||kgf||≥ 250|
|4 balls wear 1 hr 40 kg, scar diameter||ASTM D2266||mm||0, 45|
|Copper corrosion 24 hrs at 100°C||ASTM D4048||Rating||1b|
|Base oil viscosity at 40°C||ASTM D440||mm²/s||150|